Z1261P PID Free

Send Email Chat Now
Item code Specification of thickness(mm) Specification of width (mm) Gram weight (g/sqm) Length/roll (m) ackage means (mm) Min order quantity(sqm)
Z1261P 0.50 500-1200 420-450 100 - 2,000
  0.45 360 370-400 120 - 2,000
  0.45 550 370-400 120 560*290*300 2,000
  0.45 680 370-400 120 690*290*300 2,000
  0.45 810 370-400 120 830*290*300 2,000
  0.45 985 370-400 120 1010*290*300 2,000
  0.45 990 370-400 120 1010*290*300 2,000
  0.45 1000 370-400 120 1010*290*300 2,000
  0.45 1020 370-400 120 1040*290*300 2,000
  0.45 1060 370-400 120 1080*290*300 2,000
  0.40 500-1200 320-340 150 - 3,000
  0.35 500-1200 280-300 170 - 3,000
  0.30 500-1200 230-250 200 - 3,000
Item Test method Unit Fast cure type
Z1261A Z1261 / Z1261P Z1261C
Density ISO1183 g/cm³ 0.95 0.95 0.95
content TGA 26-33 26-33 28-33
Softening point DSC 55 55 55
Surface hardness GB/T531-1999 Shore A 65 65 62
Tensile strenghth (after crosslinking) ISO527-3 MPa 20 20 20
Elongation (after crosslinking) % 600 600 600
Strenghth of Extension MPa 6 6 6
UV cutoff wavelength UV-vis Nm -- 360 360
Optical transmission GB2410-80 % 91.5 91 91
Refractive index ISO489 -- 1.480 1.482 1.482
(0.45MM; 120℃,3min) Thermal shrinkage Q/ZX001-2012 MD% ≤3.0 ≤3.0 ≤10.0
TD% ≤1.0 ≤1.0 ≤3.0
(140℃,17min) Cross-linking rate Q/ZX001-2012 Gel % ≥75.0
Peeling strength With Glass Q/ZX001-2012 N/cm >60
With TPT N/cm >40
(90℃,90%RH, 1500hrs) Damp Heat resistance Yellowness index Q/ZX001-2012 △YI <3
Peeling strenghth with glass N/cm >40
(1500hrs) UV Exposure resistance Yellowness index Q/ZX001-2012 △YI <3
Peeling strenghth with glass N/cm >40
Volume resistance GB/T 1410 Ω·cm ≥1*1015
Dielectric strength GB/T1408.1 Kv/mm >28
PID resistance test (85℃,85%RH,-1000V,96H) IEC61730-2:2004 IEC61215:2005 Power loss % <5%
Operating parameters Items Extra fast cure, High transmission, PID free
Z1261 / Z1261A /Z1261P
Laminating curing parameters   135±2 140±2 145±2 150±2
Heating panel (℃)
 
Pump down time (min) 5±1 5±1 4±1 4±1
Holding time(min) 15±2 12±1 10±1 7±1

Note: Laminating process conditions shall be selected and confirmed according to the performance of laminating machine.